AlSi10Mg Alloy

AlSi10Mg is an aluminum alloy with excellent mechanical properties combined with low density, corrosion resistance and excellent castability while offering lightweight and flexible post-processing options.

Because it offers high strength, relatively high hardness and high thermal conductivity, it is used for parts which are subject to high loads.

Applications include housing and ductworks, engine parts, production tools and molds for both prototyping and manufacturing purposes.

    Properties:                                                                                   Applications:

Lightweight                                                                                   Aerospace and Automotive

High Thermal conductivity                                                        Jewelry and Art

High Strength and Hardness                                                     Prototypes

Fast building and flexible Post-processing                             Complex geometries

Excellent castability                                                                     Production tools and molds

Powder Composition (AMS 4998, ASTM F1367):

Silicon                 9.0-11.0%                 Lead                      ≤ 0.05%

Magnesium        0.2-0.45%                Manganese         ≤ 0.45%

Aluminum           Balance                  Nickel                   ≤ 0.05%

Oxygen                ≤ 0.08%                  Tin                         ≤ 0.05%

Copper                ≤ 0.05%                   Titanium               ≤0.15%

Iron                       ≤ 0.55%                   Zinc                       ≤ 0.10%

Properties (Wrought Material):

Density:                                                                    2.67 gram/cm³

Melting Point range:                                               570 – 590^oC

Thermal Conductivity:                                            120 - 180 W/mK

Coefficient of Thermal Expansion:                       20 x 10^-6 K^-1 (0 – 100^oC)

Mechanical Properties of Additive Manufactured components:

Tensile Strength (horizontal direction (XY))                460 MPa (+/- 20 MPa)

Tensile Strength (vertical direction (Z))                        460 MPa (+/- 20 MPa)

Yield Strength (horizontal direction (XY))                    270 MPa (+/- 10 MPa)

Yield Strength (vertical direction (Z))                            240 MPa (+/- 10 MPa)

Elongation (at break) (horizontal direction (XY))         9% (+/- 2%)

Elongation (at break) (vertical direction (Z))                6% (+/- 2%)

Modulus of Elasticity (horizontal direction (XY))         75 GPa (+/- 10 GPa)

Modulus of Elasticity (vertical direction (Z))                70 GPa (+/- 10 GPa)

Hardness(HRC)                                                                120 (+/- 10)